Fluorosilicone Rubber Base(uncatalyzed)
Product Name : FS261 FS271 FS351 FS360 FS361 FS362
Fluorosilicone Rubber Base(uncatalyzed) Product Name : FS261
Project |
Test Standard |
Data |
Appearance |
----- |
Kind Color of Elastomer |
Specific Gravity ( g/cm3) |
ASTM D792 |
1.45 |
Hardness ( Shore, A ) |
ASTM D2240 |
60 |
Tensile ( Kgf/cm2,Die C ) |
ASTM D412 |
85 |
Ultimate Elongation ( %, Die C ) |
ASTM D412 |
280 |
Tear Strength ( KN/m ,Die B ) |
ASTM D624 |
10 |
Compression Set ( %,175 °C /22hr ) |
ASTM D395 |
16 |
Volume Swell ( %Fuel C, 23 °C /70hr ) |
ASTM D471 |
25 |
Press Cure:170°C×15min,Vulcanizing Agent:DHBP,Dosage:0.6%
Post Cure:200°C×4hr
Fluorosilicone Rubber Base(uncatalyzed) Product Name : FS271
Project |
Test Standard |
Data |
Appearance |
--- |
Kind Color of Elastomer |
Specific Gravity ( g/cm3) |
ASTM D792 |
1.46 |
Hardness ( Shore, A ) |
ASTM D2240 |
70 |
Tensile ( Kgf/cm2,Die C ) |
ASTM D412 |
85 |
Ultimate Elongation ( %, Die C ) |
ASTM D412 |
180 |
Tear Strength ( KN/m ,Die B ) |
ASTM D624 |
10 |
Compression Set ( %,175 °C /22hr ) |
ASTM D395 |
16 |
Volume Swell ( %Fuel C, 23 °C /70hr ) |
ASTM D471 |
24 |
Press Cure:170°C×15min,Vulcanizing Agent:DHBP,Dosage:0.6%
Post Cure:200°C×4hr
Fluorosilicone Rubber Base(uncatalyzed) Product Name : FS351
Project |
Test Standard |
Data |
Appearance |
--- |
Kind Color of Elastomer |
Specific Gravity ( g/cm3) |
ASTM D792 |
1.42 |
Hardness ( Shore, A ) |
ASTM D2240 |
50 |
Tensile Stress ( Kgf/cm2,Die C ) |
ASTM D412 |
100 |
Ultimate Elongation ( %, Die C ) |
ASTM D412 |
480 |
Tear Strength ( KN/m , Die B ) |
ASTM D624 |
35 |
Compression Set ( %,175 °C /22hr ) |
ASTM D395 |
15 |
Volume Swell ( %Fuel C, 23 °C /70hr ) |
ASTM D471 |
24 |
Press Cure:170°C×15min,Vulcanizing Agent:DHBP, Dosage:0.6%
Post Cure:200°C×4hr
Fluorosilicone Rubber Base(uncatalyzed) Product Name : FS360
Project |
Test Standard |
Data |
Appearance |
--- |
Kind Color of Elastomer |
Specific Gravity ( g/cm3) |
ASTM D792 |
1.43 |
Hardness ( Shore, A ) |
ASTM D2240 |
60 |
Tensile Stress ( Kgf/cm2,Die C ) |
ASTM D412 |
80 |
Ultimate Elongation ( %, Die C ) |
ASTM D412 |
350 |
Tear Strength ( KN/m , Die B ) |
ASTM D624 |
30 |
Compression Set ( %,175 °C /22hr ) |
ASTM D395 |
15 |
Volume Swell ( %Fuel C, 23 °C /70hr ) |
ASTM D471 |
25 |
Press Cure:170°C×15min,Vulcanizing Agent:DHBP, Dosage:0.6%
Post Cure:200°C×4hr
Fluorosilicone Rubber Base(uncatalyzed) Product Name : FS361
Project |
Test Standard |
Data |
Appearance |
--- |
Kind Color of Elastomer |
Specific Gravity ( g/cm3) |
ASTM D792 |
1.43 |
Hardness ( Shore, A ) |
ASTM D2240 |
66 |
Tensile Stress ( Kgf/cm2,Die C ) |
ASTM D412 |
100 |
Ultimate Elongation ( %, Die C ) |
ASTM D412 |
380 |
Tear Strength ( KN/m , Die B ) |
ASTM D624 |
25 |
Compression Set ( %,175 °C /22hr ) |
ASTM D395 |
15 |
Volume Swell ( %Fuel C, 23 °C /70hr ) |
ASTM D471 |
25 |
Press Cure:170°C×15min,Vulcanizing Agent:DHBP, Dosage:0.6%
Post Cure:200°C×4hr
Fluorosilicone Rubber Base(uncatalyzed) Product Name : FS362
Project |
Test Standard |
Data |
Appearance |
--- |
Kind Color of Elastomer |
Specific Gravity ( g/cm3) |
ASTM D792 |
1.43 |
Hardness ( Shore, A ) |
ASTM D2240 |
60 |
Tensile ( Kgf/cm2,Die C ) |
ASTM D412 |
100 |
Ultimate Elongation ( %, Die C ) |
ASTM D412 |
480 |
Tear Strength ( KN/m ,Die B ) |
ASTM D624 |
35 |
Compression Set ( %,175 °C /22hr ) |
ASTM D395 |
15 |
Volume Swell ( %Fuel C, 23 °C /70hr ) |
ASTM D471 |
25 |
Press Cure:170°C×15min,Vulcanizing Agent:DHBP,Dosage:0.6%
Post Cure:200°C×4hr
|